Influence of postpolymerization time and atmosphere on the mechanical properties, degree of conversion, and cytotoxicity of denture bases produced by digital light processing.

Lee, Won-Jun; Jo, Ye-Hyeon; Yoon, Hyung-In (2023). Influence of postpolymerization time and atmosphere on the mechanical properties, degree of conversion, and cytotoxicity of denture bases produced by digital light processing. The journal of prosthetic dentistry, 130(2), 265.e1-265.e7. Elsevier 10.1016/j.prosdent.2023.05.008

Text 1-s2.0-S0022391323003384-main.pdf - Published Version Restricted to registered users only Available under License Publisher holds Copyright. Download (1MB) | Request a copy

STATEMENT OF PROBLEM

Studies on the effects of postprocessing conditions on the physical properties, degree of conversion (DC), and biocompatibility of denture bases produced by digital light processing are lacking.

PURPOSE

The purpose of this in vitro study was to evaluate the effects of the atmosphere during postpolymerization and of postpolymerization time on the flexural strength, Vickers hardness, DC, cytotoxicity, and residual monomer content of denture bases.

MATERIAL AND METHODS

Six different groups of bar- and disk-shaped specimens from the denture base resin were produced, considering 2 different atmospheres (air and nitrogen) and 3 different postpolymerization times (5, 10, and 20 minutes). To determine the physical properties, the flexural strength and Vickers hardness were measured. Fourier transform infrared spectrometry was used to calculate DC. Cytotoxicity was assessed from the effect on human gingival fibroblasts. The residual monomer content was determined by using high-performance liquid chromatography. Based on the normality test by the Shapiro-Wilk method, a nonparametric factorial analysis of variances was conducted (α=.05).

RESULTS

A significant interaction was detected between the atmosphere and postpolymerization time for hardness (P<.001) but no interaction for strength, DC, or cytotoxicity (P=.826, P=.786, and P=.563, respectively). Hardness was significantly affected by the postpolymerization time in the groups with the nitrogen atmosphere (P<.001). DC was significantly affected by the atmosphere (P=.012), whereas strength and cytotoxicity were not (P=.500 and P=.299, respectively). Cytotoxicity was significantly affected by the postpolymerization time (P<.001), but strength and DC were not (P=.482 and P=.167, respectively). Residual monomers were not detected after ≥10-minute postpolymerization time.

CONCLUSIONS

The atmosphere significantly affected hardness and DC, whereas the postpolymerization time significantly affected hardness, DC, cytotoxicity, and residual monomer content. Denture bases produced in a nitrogen atmosphere and with the 10-minute postpolymerization time showed sufficient hardness, DC, and no cytotoxicity.

Interest & Impact

Downloads

0 since deposited on 27 Jun 2023
0 in the past 12 months

Citations

5 Citations in Web of Science ®
6 Citations in Scopus

Search

in Google Scholar™

Services

Actions (login required)

Edit item

Actions (login required)

Edit item