Aluminum incorporation into magnesium silicate hydrate (M-S-H)

Bernard, Ellina; Lothenbach, Barbara; Cau-Dit-Coumes, Céline; Pochard, Isabelle; Rentsch, Daniel (2020). Aluminum incorporation into magnesium silicate hydrate (M-S-H). Cement and concrete research, 128, p. 105931. Elsevier 10.1016/j.cemconres.2019.105931

Text 1-s2.0-S0008884619305204-main.pdf - Published Version Restricted to registered users only Available under License Publisher holds Copyright. Download (2MB)

The incorporation of aluminum in magnesium silicate hydrate (M-S-H) phases was investigated. Magnesium (alumino) silicate hydrate (M-(A-)S-H) with Mg/Si ratios equal to 1.1 or 1.7 and Al/Si ranging from 0 to 0.2 were synthetized in batch experiments and equilibrated at 20, 50 and 70 °C. pH values between 9 and 10.5 were observed and aluminum up to Al/Si ~0.15–0.18 was incorporated in M-(A-)S-H. Thermogravimetric analysis (TGA), X-ray diffraction (XRD), X-ray pair distribution function (PDF) analysis, transmission electron microscopy (TEM), 29Si and 27Al MAS NMR data showed that the M-(A-)S-H phases formed were similar to M-S-H with limited coherent size and a comparable polymerization degree of the tetrahedral silicates. Aluminum was incorporated in both tetrahedral and octahedral sites of M-S-H, while no aluminum was present as exchangeable cation on the surface sites.

Interest & Impact

Downloads

2 since deposited on 05 Dec 2019
0 in the past 12 months

Citations

5 Citations in Web of Science ®
6 Citations in Scopus

Search

in Google Scholar™

Services

Actions (login required)

Edit item

Actions (login required)

Edit item