Bone apposition to a titanium-zirconium alloy implant, as compared to two other titanium-containing implants

Saulacic, Nikola; Bosshardt, Dieter; Bornstein, Michael; Berner, Simon; Buser, Daniel (2012). Bone apposition to a titanium-zirconium alloy implant, as compared to two other titanium-containing implants. European cells & materials eCM, 23, pp. 273-286. Aberystwyth (UK): University of Wales

Preview

Text v023a21.pdf - Published Version Available under License Publisher holds Copyright. Download (2MB) | Preview

Implants made of commercially pure titanium (cpTi) are widely and successfully used in dentistry. For certain indications, diameter-reduced Ti alloy implants with improved mechanical strength are highly desirable. The aim was to compare the osseointegration of titanium-zirconium (TiZr) and cpTi implants with a modified sandblasted and acid-etched (SLActive) surface and with a Ti6Al4V alloy that was sand-blasted and acid-washed. Cylindrical implants with two, 0.75 mm deep, circumferential grooves were placed in the maxilla of miniature pigs and allowed to heal for 1, 2, 4 and 8 weeks. Undecalcified toluidine blue-stained ground sections were produced. Surface topography, area fraction of tissue components, and bone-to-implant contact (BIC) were determined. All materials showed significantly different surface roughness parameters. The amount of new bone within the implant grooves increased over time, without significant differences between materials. However, BIC values were significantly related to the implant material and the healing period. For TiZr and cpTi implants, the BIC increased over time, reaching values of 59.38 % and 76.15 % after 2 weeks, and 74.50 % and 84.67 % after 8 weeks, respectively. In contrast, the BIC for Ti6Al4V implants peaked with 42.29 % after 2 weeks followed by a decline to 28.60 % at 8 weeks. Significantly more surface was covered by multinucleated giant cells on Ti6Al4V implants after 4 and 8 weeks. In conclusion, TiZr and cpTi implants showed faster osseointegration than Ti6Al4V implants. Both chemistry and surface topography might have influenced the results. The use of diameter-reduced TiZr implants in more challenging clinical situations warrants further documentation in long-term clinical studies.

Interest & Impact

Downloads

852 since deposited on 04 Oct 2013
119 in the past 12 months

Citations

5 Citations in Web of Science ®
6 Citations in Scopus

Search

in Google Scholar™

Services

Actions (login required)

Edit item

Actions (login required)

Edit item