Bastian, Johannes Dominik; Egli, Rainer J; Ganz, Reinhold; Hofstetter, Willy; Leunig, Michael (2011). Chondrocytes within osteochondral grafts are more resistant than osteoblasts to tissue culture at 37°C. Journal of investigative surgery, 24(1), pp. 28-34. New York, N.Y.: Taylor & Francis 10.3109/08941939.2010.523511
Full text not available from this repository.It is proposed that an ideal osteochondral allograft for cartilage repair consists of a devitalized bone but functional cartilage. The different modes of nutrient supply in vivo for bone (vascular support) and cartilage (diffusion) suggest that a modulation of storage conditions could differentially affect the respective cells, resulting in the proposed allograft. For this purpose, osteochondral tissues from porcine humeral heads were either cultured at 37°C for up to 24 hr or stored at 4°C for 24 hr, the temperature at which osteochondral allografts are routinely stored. Functionality of the cells was assessed by in situ hybridization for transcripts encoding collagen types I and II. At 37°C, a time-dependent significant reduction of the bone surface covered with functional cells was observed with only 5% ± 5% coverage left at 24 hr compared with 41% ± 10% at 0 hr. Similarly, cartilage area containing functional cells was significantly reduced from 84% ± 7% at 0 hr to 70% ± 3% after 24 hr. After 24 hr at 4°C, a significantly reduced amount of functional cells covering bone surfaces was observed (27% ± 5%) but not of cells within the cartilage (79% ± 8%). In the applied experimental setup, bone cells were more affected by tissue culture at 37°C than cartilage cells. Even though chondrocytes appear to be more sensitive to 37°C than to 4°C, the substantially reduced amount of functional bone cells at 37°C warrants further investigation of whether a preincubation of osteochondral allografts at 37°C--prior to regular storage at 4°C--might result in an optimized osteochondral allograft with devitalized bone but viable cartilage.
Actions (login required)
 |
Edit item |