Highly Efficient IR to NIR Upconversion in Gd2O2S: Er3+ for Photovoltaic Applications

Martín-Rodríguez, Rosa; Fischer, Stefan; Ivaturi, Aruna; Froehlich, Benjamin; Krämer, Karl; Goldschmidt, Jan C.; Richards, Bryce S.; Meijerink, Andries (2013). Highly Efficient IR to NIR Upconversion in Gd2O2S: Er3+ for Photovoltaic Applications. Chemistry of materials, 25(9), pp. 1912-1921. Washington, D.C.: American Chemical Society 10.1021/cm4005745

Text cm4005745.pdf - Published Version Restricted to registered users only Available under License Publisher holds Copyright. Download (4MB)

Upconversion (UC) is a promising option to enhance the efficiency of solar cells by conversion of sub-bandgap infrared photons to higher energy photons that can be utilized by the solar cell. The UC quantum yield is a key parameter for a successful application. Here the UC luminescence properties of Er3+-doped Gd2O2S are investigated by means of luminescence spectroscopy, quantum yield measurements, and excited state dynamics experiments. Excitation into the maximum of the 4I15/2 → 4I13/2 Er3+ absorption band around 1500 nm induces very efficient UC emission from different Er3+ excited states with energies above the silicon bandgap, in particular, the emission originating from the 4I11/2 state around 1000 nm. Concentration dependent studies reveal that the highest UC quantum yield is realized for a 10% Er3+-doping concentration. The UC luminescence is compared to the well-known Er3+-doped β-NaYF4 UC material for which the highest UC quantum yield has been reported for 25% Er3+. The UC internal quantum yields were measured in this work for Gd2O2S: 10%Er3+ and β-NaYF4: 25%Er3+ to be 12 ± 1% and 8.9 ± 0.7%, respectively, under monochromatic excitation around 1500 nm at a power of 700 W/m2. The UC quantum yield reported here for Gd2O2S: 10%Er3+ is the highest value achieved so far under monochromatic excitation into the 4I13/2 Er3+ level. Power dependence and lifetime measurements were performed to understand the mechanisms responsible for the efficient UC luminescence. We show that the main process yielding 4I11/2 UC emission is energy transfer UC.

Interest & Impact

Downloads

2 since deposited on 11 Dec 2013
0 in the past 12 months

Citations

5 Citations in Web of Science ®
6 Citations in Scopus

Search

in Google Scholar™

Services

Actions (login required)

Edit item

Actions (login required)

Edit item