Effect of simulated brushing and disinfection on the surface roughness and color stability of CAD-CAM denture base materials.

Çakmak, Gülce; Donmez, Mustafa Borga; Akay, Canan; Atalay, Sevda; Silva de Paula, Marcella; Schimmel, Martin; Yilmaz, Burak (2022). Effect of simulated brushing and disinfection on the surface roughness and color stability of CAD-CAM denture base materials. Journal of the mechanical behavior of biomedical materials, 134, p. 105390. Elsevier 10.1016/j.jmbbm.2022.105390

Preview

Text 1-s2.0-S1751616122002983-main.pdf - Published Version Available under License Creative Commons: Attribution (CC-BY). Download (1MB) | Preview

PURPOSE

To evaluate the effect of simulated brushing and chemical disinfection on the surface roughness and color stability of CAD-CAM denture base materials and to compare with those of a heat-cured denture base material.

MATERIAL AND METHODS

Disk-shaped specimens (Ø 10mm × 2 mm) were prepared from 3 CAD-CAM denture base resins (AvaDent, Ava; Merz M-PM, Merz; Polident d.o.o, Poli) and a heat-cured polymethylmethacrylate resin (Promolux, Conv) (n = 30). After polishing, baseline surface roughness (Ra) and color coordinates were measured. The measurements were repeated after 20000 cycles of simulated brushing, and the specimens were divided into 3 groups according to disinfection protocol (distilled water, 1% sodium hypochlorite (NaOCl), and effervescent tablet) (n = 10). After 9 cleaning cycles over a period of 20 days, Ra and color coordinates were remeasured. Color differences (ΔE00) were calculated by using CIEDE2000 formula. One-way analysis of variance (ANOVA) and pairwise t-tests were used to analyze Ra and ΔE00 data, while repeated measures ANOVA test was used to compare baseline, after brush, and after disinfection Ra values (α = 0.05).

RESULTS

Brushing did not affect the Ra values of tested materials (P ≥ .08). Both before and after brushing, Merz and Conv had higher Ra values than Poli and Ava (P < .001). Among disinfectants, effervescent tablet led to the lowest Ra for Merz (P = .003) and the highest Ra for Poli (P ≤ .039). Only NaOCl resulted in significant differences among the Ra of materials (P < .001), as Merz and Conv had higher Ra values than Poli (P ≤ .002). Repeated measures ANOVA revealed that effervescent tablet disinfection of Merz led to lower Ra values than those of baseline and after brushing (P ≤ .042). After brushing, Ava and Conv had higher ΔE00 values compared with Merz and Poli (P ≤ .015). When compared with other disinfection protocols, effervescent tablet led to higher ΔE00 values for Merz and Poli (P < .001). Significant differences were observed among materials when NaOCl was used; Conv had higher ΔE00 values than Ava and Merz (P = .004).

CONCLUSIONS

Brushing did not increase the surface roughness of materials. Disinfection protocol's effect on the surface roughness varied. The effect of brushing on the color of materials varied; color of Ava and Conv was affected from brushing more than the other materials. Color stability of materials varied depending on the disinfection protocol. Effervescent tablet caused higher color change with Merz and Poli compared with other disinfectants. NaOCl led to small color change for Poli, Ava, and Merz materials.

Interest & Impact

Downloads

66 since deposited on 04 Aug 2022
38 in the past 12 months

Citations

5 Citations in Web of Science ®
6 Citations in Scopus

Search

in Google Scholar™

Services

Actions (login required)

Edit item

Actions (login required)

Edit item